T-1 Type B
| Thickness | 3/16” to 2”, incl. |
|---|---|
| Yield Strength (Extension Under Load), min. | 10000 psi |
| Tensile Strength | 115000/135000 psi |
| Elongation in 2 inches, % min. | 18 |
| Reduction of Area, % min., Plates 3/4” and under | 40 |
| Reduction of Area, % min, Plates over 3/4” to 2”, incl. | 50 |
ASTM A514 - Grade H - Chemical Composition
| C | Mn | P Max. | S Max. | Si | Ni | Cr | Mo | V | Cu | B min. |
|---|---|---|---|---|---|---|---|---|---|---|
| .12/.21 | .95/1.3 | 0.035 | 0.04 | .20/.35 | .30/.7 | .40/.65 | .20/.3 | .03.08 | 0.0005 |
*0.20 / 0.40 if specified when added corrosion resistance is desired.
ASTM A514 Grade H - Cold Forming Data For Plates
| Thickness | Suggested Minimum Inside Radius |
|---|---|
| Up to 1” Incl. | 2t |
| Over 1” to 2”, incl. | 3t |
*U.S. Patent No. 2,858,206
"T-1" is a registered trademark of United States Steel
t = Times (x) Thickness